應用范圍 - 固體潤滑皮膜適合于的鈦金屬的熱成形中的成形操作,以避免磨損。此產品也非常適合壓鑄鋁和鋅金屬。也被廣泛使用在管的彎曲或擠
TIOFORM LF22
is a lubricating coating intended for use in the hot forming of titanium metals to prevent galling in the forming operation. This product is also excellent for die casting aluminum and zinc metals. It has also been found to be of considerable value when used in tube bending or extruding. The product is designed to function as a boundary lubricant in cold forming operations and in hot forming at temperatures up to and exceeding 1500°F.
Approvals/References/Specs
Boeing Specification: BAC 5756, Ty. IV
Hughes Aircraft Co. Specification: HP 1-27
Lockheed Martin Corporation-Aircraft Div. Specification: LAC 37-674
Lockheed Martin Corporation-Aircraft Div. Specification: LCP 70-1099
Lockheed Martin Corporation-Aircraft Div. Specification: STM 37-103
Boeing McDonnell Douglas Specification: DPM 3481
Boeing McDonnell Douglas Specification: DPM 5666
Boeing McDonnell Douglas Specification: DPS 10150
Boeing McDonnell Douglas Specification: DPS 44120
Boeing McDonnell Douglas Specification: PS 14211
Northrop Grumman Corporation Specification: L-8, Rev. C
Northrop Grumman Corporation Specification: MA-105
Pratt & Whitney Specification: PMC 9536
Pratt & Whitney Specification: PWA 113C thru E
Precision Castparts Corp. Specification: III-57-02
Rockwell Specification: LBO225-001
Rockwell International Specification: STO102LA-0005, Rev. B
Rockwell International Specification: STO225GB0001, Rev. B
Physical Characteristics: The coating is a composition of lubricating pigments suspended in a modified high temperature resin binder with Toluene as the carrier. It is dull black in color and will not blister, crack or peel.
Temperature: This material may be used in a temperature range of -65°F to above 1500°F.
Use: The coating should be applied a short period of time before the mechanical operation to allow evaporation of the solvent carrier. This will allow a clean release from the mold and will prevent galling and damage to the materials in the mechanical operation.
Application: Four easy steps are involved in the use of
TIOFORM LF22
a) The surface of the metal should be cleaned. The methods used will vary depending upon the mechanical operation to be performed. In the hot forming of titanium, standard practice is to cold form followed by various rinses in water, methyl ethyl ketone, solvent cleaning, alkaline cleaning and pickling. This application of Formkote and the hot forming operation. In die casting, extruding, tube bending, etc., the surface to be coated must be cleaned by a solvent to ensure the removal of any contamination.
b) Apply the coating by spray, brush, dip or swab application. The product is available in aerosol or quart, gallon and 5-gallon containers. The material is supplied ready for application, but additional thinning may be accomplished with the use of Toluene as required. Best results are usually obtained with a coating thickness of 0.5 to 1.5 mils.
c) Perform required operation hot forming, die casting, extruding etc.
d) After the mechanical operation,
TIOFORM LF22
s removed by various methods. During a hot forming operation, the majority of the lubricating film is burned off leaving a slight residue. This is removed by solvent washes, alkaline cleaning, pickling, or vapor honing, followed by various demineralized water rinse and drying. After a cold operation, the coating has not been subjected to temperatures, which will cause polymerization and can be removed by simple solvent cleaning, leaving no trace of lubricant film.
This product is approved and is being currently used by major fabricators of titanium alloys and various other metals.