Alseal HX is a coating composition formulated for protecting ferrous alloys from both high temperature heat oxidation and at
the same time offer sacrificial (cathodic) protection to the base metal. HX was formulated especially for application to
headers, providing a smooth finish that may be burnished to a mirror shine.
Because of its high temperature capabilities, it offers excellent protection when exposed to cyclic high temperature and
corrosive salt environments, continuing to provide sacrificial properties at temperatures to 1150F. Although a ceramic
coating, it combines thermal stability, excellent adhesion and hardness, along with good flexibility... a property not found in
most ceramic coatings. As mentioned above it offers salt corrosive protection to 1150°F. At about 1200°F. the aluminum
oxidizes to a point where it no longer provides its excellent sacrificial properties, however, it will continue to offer excellent
heat oxidation continuously to 1600°F. and in some cases, depending on metal substrate, has offered heat oxidation
protection to 2200°F.
Tests have been conducted using low carbon steel alloys. There was no loss of weight after several weeks continuous
exposure at 1000°F. After exposure to 5% salt spray for 1000 hours, there was no evidence of corrosion.
Further, the coating formed from Alseal HX composition offers superb thermal shock resistance. The coated metal will not
crack, spall, or fail after shocking from 1100°F. to room temperature repeatedly.
Surface Preparation
Special care must be exercised in the preparation of the surface for all high quality, premium performance coatings.
1) Degreasing. All oil, grease and other organic deposits must be removed by suitable degreasing operation or by heating
parts to temperature sufficiently high to facilitate removal.
2) Cleaning and Roughening. All old coats, mill scale, rust, or other tightly adherent deposits must be removed by a
method such as dry grit blasting or vapor blasting. Grit blast, using clean aluminum oxide AL2
O3) grit, is the recommended
cleaning procedure which is necessary for maximum adhesion to steel, although other abrasive methods may be satisfactory由于其耐高溫能力,它提供了出色的保護,當暴露在循環高溫和腐蝕性鹽的環境中,繼續在溫度1150提供犧牲性能* F。盡管陶瓷涂層,它結合了熱穩定性,優異的附著力和硬度,以及良好的柔韌性......一個屬性不是在大多數陶瓷涂層找到。如上所述,它提供了鹽的腐蝕防護1150F。在約1200 F的鋁氧化成一個點,它不再提供其優異犧牲性能,但是,它會繼續不斷地提供優良的熱氧化1600 F ,在某些情況下,根據金屬基板,提供了熱氧化保護到2200F
從HX3200組合物形成的涂層提供了極好的抗熱震性。該涂層的金屬不會開裂,剝落,或反復后令人震驚的失敗來自1100F到室溫。